Ferritic Stainless Steel发表评论(0)编辑词条

Ferritic Stainless Steel

Chromium is the main alloy element in this group. It may reach amounts higher than 25%, in combination with carbon content lower than 0.2%. They cannot be hardened through quenching (martensitic transformations). They are more stainless than martensitic steels under oxidizing conditions or in an atmospheric milieu. Since the grains are not refined through heat treatment, additional care must be taken when reheating them at high temperatures. Due to their high content of chromium, these steels tend to weaken when exposed to 500ºC for a long time, what requires attention when selecting the pieces to be applied. They have good cold conforming under any conditions because of their ferritic structure (soft). They have magnetic sensitivity (ferromagnetism).

铁素体不锈钢

    在使用状态下以铁素体组织为主的不锈钢。含铬量在11%~30%，具有体心立方晶体结构。

    这类钢一般不含镍，有时还含有少量的Mo、ti、Nb等到元素，这类钢具导热系数大，膨胀系数小、抗氧化性好、抗应力腐蚀优良等特点，多用于制造耐大气、水蒸气、水及氧化性酸腐蚀的零部件。

    这类钢存在塑性差、焊后塑性和耐蚀性明显降低等缺点，因而限制了它的应用。炉外精炼技术（AOD或VOD）的应用可使碳、氮等间隙元素大大降低，因此使这类钢获得广泛应用。
铁素体(ferrite，缩写：FN)
　　即α-Fe和以它为基础的固溶体，具有体心立方点阵。亚共析成分的奥氏体通过先共析析出形成铁素体。这部分铁素体称为先共析铁素体或组织上自由的铁素体。随形成条件不同，先共析铁素体具有不同形态，如等轴形、沿晶形、纺锤形、锯齿形和针状等。铁素体还是珠光体组织的基体。在碳钢和低合金钢的热轧（正火）和退火组织中，铁素体是主要组成相；铁素体的成分和组织对钢的工艺性能有重要影响，在某些场合下对钢的使用性能也有影响。
　　纯铁在912℃以下为具有体心立方晶格（注1）的α-Fe。碳溶于α-Fe中的间隙固溶体称为铁素体，以符号F表示。由于α-Fe是体心立方晶格结构，它的晶格间隙很小，因而溶碳能力极差，在727℃时溶碳量最大，可达0.0218％,随着温度的下降溶碳量逐渐减小，在600％时溶碳量约为0.0057％，在室温时溶碳量几乎等于零。因此其性能几乎和纯铁相同，其数值如下：
　　抗拉强度 180—280MN/平方米
　　屈服强度 100—170MN/平方米
　　延伸率 30--50％
　　断面收缩率 70--80％
　　冲击韧性 160—200J/平方厘米
　　硬度 HB 50—80
　　由此可见，铁素体的强度、硬度不高，但具有良好的塑性与韧性。
　　铁素体的显微组织与纯铁相同，呈明亮的多边形晶粒组织，有时由于各晶粒位向不同，受腐蚀程度略有差异，因而稍显明暗不同。
　　铁素体在770℃以下具有铁磁性，在770℃以上则失去铁磁性。
　　（铁素体的居里点为770℃）
　　注1：体心立方晶格的晶胞是一个立方体，在体心立方晶胞的每个角上和晶胞中心都排列一个原子。可见，体心立方晶胞每个角上的原子为相邻的八个晶胞所共有，每个晶胞实际上只占有1/8个原子。而中心的原子却为该晶胞所独有。所以，体心立方晶胞中原子数为8*1/8+1=2个。碳原子存在于四面、八面体间隙。